Strength, aesthetics and improved processing
Kalix® HPPA (high-performance polyamide) is designed for structural components used in smart mobile electronic devices. They provide high strength, rigidity and a high-quality surface finish along with improved processing.
Kalix® HPPA products are highly glass-filled compounds that can replace metal in structural mobile electronic components where strength, rigidity and aesthetics are important such as housings, covers, chassis and frames.
Different base resins are used to tailor performance and processing requirements. Processing improvements include lower warpage, reduced shrinkage, and low to no flash.
Bio-sourced and halogen-free flame retardant grades are available.
|KALIX® HPPA BASE RESINS|
|Kalix® HPPA||Base Resin*||Key Characteristics|
|9000 Series||PARA||General purpose|
|2000 Series||PA 6, 10||High impact resistance, bio-sourced|
|5000 Series||MXD6, variant||Halogen-free flame retardant, low warpage|
* PA = polyamide; PPA = polyphthalamide; MXD = meta-xylylene diamine; PARA = polyarylamide
|Kalix® 9000 Series|
|9950||50% glass fiber, general purpose|
|9945 HFFR||45% glass fiber, halogen-free flame retardant|
|Kalix® 2000 Series, Bio-sourced|
|2955||55% glass fiber, high impact, lower warpage than 2855|
|2855||55% glass fiber, high impact, higher strength, stiffness and ductility than 2955|
|Kalix® 5000 Series|
|5950 HFFR||50% glass fiber, halogen-free flame retardant, low warpage|
Tensile Strength vs. Tensile Modulus
ISO 527 test method
Unnotched Izod Impact vs. Tensile Elongation at Break
ISO 180 & ISO 527 test methods
|Kalix® 9950||HB at 0.6mm, all colors|
|Kalix® 9945 HFFR||V0 at 0.4mm, all colors|
|Kalix® 5950||V0 at 0.4mm, all colors, 5VA at 1.5 mm, all colors|
Surface appearances vary in the level of gloss and surface roughness. Kalix® 5950 HFFR has the highest gloss and lowest surface roughness, giving it the best surface appearance overall.
ISO 1997 & ISO 2813 test methods (injection mold temperature, 120°C)
Color MatchingKalix® HPPA products can be matched to a wide color spectrum, including light and bright colors. They can also be painted with coatings commonly used in the mobile electronic device industry
Depending on the grade, Kalix® HPPA materials provide lower warpage, reduced shrinkage, and low to no flash. These improvements result in tighter dimensional tolerances and more cost-effective manufacturing due to fewer secondary operations such as deflashing.
|Kalix® 9000 series||80-120 (176-248)||280-310 (536-590)|
|Kalix® 2000 series||80-120 (176-248)||270-300 (518-572)|
|Kalix® 5000 series||115-130 (239-266)||270-300 (518-572)|
Solvay internal test methods
Solvay internal test methods
ISO 62 test method, in water after 24 hours at 23°C
Kalix® 2000 products contain monomers from the sebacic acid chain derived from non-food competing and GMO-free (genetically modified organism) castor oil. Their renewable content is calculated according to ASTM D6866 test method for determining bio-based carbon content.
|Product Series||Bio-Based Content*||Base Resin|
|Kalix® 2000 base resin||61%||PA 6, 10|
* As determined according to ASTM D6866.
** Bio-content corrected for glass fiber loading.